SUNDY Polyvinyl Alcohol PVA NJ-I(G-X1) 088-05 With Defoamer
Discription:
Polyvinyl alcohol 0588 flakes are made of advanced technology and process, using vinyl acetate produced by petroleum production method as raw material, methanol as solvent, azobisisobutyronitrile as initiator, through polymerization, alcoholysis and other processes. It is a water-soluble environment-friendly high molecular polymer, non-toxic and non-polluting, with good film-forming properties, emulsifying properties, bonding properties and spinning properties. It forms films with excellent adhesion, solvent resistance, abrasion resistance, tensile strength and oxygen barrier properties. Because polyvinyl alcohol has both hydrophilic and hydrophobic functional groups, it has interface activity, so polyvinyl alcohol can be used as a protective colloid for polymer emulsification and suspension polymerization.
Polyvinyl Alcohol is a water-soluble polymer material with the chemical formula [CH2CH(OH)]n. It is a synthetic polymeric material that is important in papermaking, textile packaging sizing, and as a thickener and emulsion stabilizer in PVAC adhesive formulations. Furthermore, this substance can be used for different kinds of coatings and 3D printing. In addition, polyvinyl alcohol is a colorless, odorless substance that is usually marketed in the form of beads or an aqueous solution.
Usage:
1. The warp sizing mainly prepared by PVA is a high-efficiency synthetic sizing agent and fabric processing agent in the sizing agent. It has good adhesion to cotton, hemp, polyester, vinylon and viscose fibers, and the sizing film is colorless and transparent. , toughness, wear resistance, sun resistance, high mechanical strength. It can reduce the breakage rate of the cloth machine. Due to the small amount of sizing, the woven cloth feels crisp, smooth and delicate, the cloth surface is not rough, and the number of windings can be increased, and the desizing is also very easy. PVA can also be used as a fabric finishing agent, often mixed with urea and formaldehyde. When the fabric is baked and melted at high temperature, a chemical reaction occurs between the two, making the Resin more flexible, thereby improving the stiffness and elasticity of the processed fabric. The stiffness of the fabric can be adjusted by the amount of PVA.
2. PVA has strong adhesion in papermaking and strong film formation. It can be used instead of starch and casein or used in combination with them. It can be used as a coating paper vehicle, or as a glue for coated paper, wear-resistant paper, base paper, kraft paper. Surface sizing can improve the wear resistance, folding resistance and tear resistance of the paper, and improve the gloss, smoothness and printing adaptability. PVA water solution can be used to replace water glass, starch or used in combination for printing and binding, carton, cardboard, paper tube, etc.
3. The adhesive is a series of adhesives made of PVA as the main raw material. It has good adhesion to paper, cloth and wood. It has a wide range of uses. Materials Bonded board, leather, decoration and other industries have a large market, and some inorganic substances can be added, such as: clay, bentonite, alumina, titanium oxide, etc. to increase the bonding strength. Formaldehyde-free, water-resistant isocyanate-based adhesives can also be developed.
4. Film The film made of PVA has good transparency, high tensile and crack resistance, good moisture permeability, good heat insulation, oil resistance, organic drug resistance, and no static electricity, so it is suitable for textile packaging. It can also be used as food packaging, non-toxic, odorless, non-polluting, degradable, and can be compounded with polyethylene, polypropylene, etc., used as instrument packaging, and can also be used for printing and plate making.
5. Acetalized derivatives PVA and formaldehyde, acetaldehyde, butyraldehyde or other aldehydes or ACID catalysts are present to generate acetalized PVA derivatives, which further improves the water resistance and adhesion of polyvinyl alcohol. Formal compounds are widely used in interior wall coatings, construction adhesives (such as 107 glue) sponges, etc. Butyral compounds have good adhesion to glass, etc., and can be used in coatings, leather, porcelain paper, aluminum foil, copper-clad plates, safety glass, etc.
6. The fiber raw material PVA is the vinylon fiber obtained by washing, dissolving, spinning, and formal treatment. It can be blended with wool, cotton, viscose and other fibers to make vinylon products, non-woven fabrics, and geotextiles. It is widely used in clothing and industrial applications. Cord, fishing net rope, tarpaulin, agricultural, sanitary materials, etc. PVA can also be used to develop and manufacture high-strength and high-modulus PVA fibers to replace asbestos and to be used as reinforcing materials for cement products, and has a very broad prospect. In addition, it can also be used to manufacture water-soluble fibers, flame-retardant fibers, hollow fibers, and protein fibers.
Specification:
| Items | Degree of alcoholysis (Mol)% | viscosity (mPa.s) | Volatile content % ≤ | ash content % ≤ | pH | Purity % ≥ |
| 100-27S | 99.5～100.0 | 23.0～29.0 | 6.0 | 0.8 | - | 92.0 |
| 100-40 | 99.5～100.0 | 35.0～45.0 | 6.0 | 0.8 | - | 92.0 |
| 100-78 | 99.5～100.0 | 73.0～83.0 | 6.0 | 0.8 | - | 92.0 |
| 098-03 | 98.0～98.8 | 3.2～4.0 | 5.0 | 0.7 | 5.0～7.0 | 94.0 |
| 098-04 | 98.0～98.8 | 4.0～5.0 | 5.0 | 0.5 | 5.0～7.0 | 94.0 |
| 098-10 | 98.0～98.8 | 8.0～12.0 | 5.0 | 0.5 | 5.0～7.0 | 94.0 |
| 098-15 | 98.0～98.8 | 13.0～17.0 | 5.0 | 0.5 | 5.0～7.0 | 94.0 |
| 098-20 | 98.0～98.8 | 18.0～22.0 | 5.0 | 0.5 | 5.0～7.0 | 94.0 |
| 098-27 | 98.0～98.8 | 23.0～29.0 | 5.0 | 0.5 | 5.0～7.0 | 94.0 |
| 098-30 | 98.0～98.8 | 28.0～32.0 | 5.0 | 0.5 | 5.0～7.0 | 94.0 |
| 097-29 | 96.0～98.0 | 27.0～31.0 | 5.0 | 0.5 | 5.0～7.0 | 94.0 |
| 097-60 | 96.0～98.0 | 56.0～66.0 | 5.0 | 0.5 | 5.0～7.0 | 94.0 |
| 092-53 | 91.0～93.0 | 48.0～58.0 | 5.0 | 0.5 | 5.0～7.0 | 94.0 |
| 088-03 | 86.5～88.5 | 3.0～4.0 | 5.0 | 0.7 | 5.0～7.0 | 94.0 |
| 088-05 | 86.5～88.5 | 4.5～6.0 | 5.0 | 0.5 | 5.0～7.0 | 94.0 |
| 088-08 | 86.5～88.5 | 8.0～10.0 | 5.0 | 0.5 | 5.0～7.0 | 94.0 |
| 088-13 | 86.5～88.5 | 12.0～14.0 | 5.0 | 0.5 | 5.0～7.0 | 94.0 |
| 088-20 | 86.5～88.5 | 21.0～24.5 | 5.0 | 0.4 | 5.0～7.0 | 94.0 |
| 088-26 | 86.5～88.5 | 24.0～28.0 | 5.0 | 0.5 | 5.0～7.0 | 94.0 |
| 088-35 | 86.5～88.5 | 29.0～34.0 | 5.0 | 0.3 | 5.0～7.0 | 94.0 |
| 088-40 | 86.5～88.5 | 38.0～42.0 | 5.0 | 0.5 | 5.0～7.0 | 94.0 |
| 088-50 | 86.5～88.5 | 45.0～55.0 | 5.0 | 0.3 | 5.0～7.0 | 94.0 |
| 080-44 | 78.0～82.0 | 42.0～52.0 | 5.0 | 0.5 | 5.0～7.0 | 94.0 |
| 088-60 | 86.5～88.5 | 56.0～66.0 | 5.0 | 0.5 | 5.0～7.0 | 94.0 |
| 086-03 | 85.0～87.0 | 3.4～4.2 | 5.0 | 0.4 | 5～7 | 93.5 |
| 098-05 | 98.0～99.0 | 5.0～6.5 | 5.0 | 0.5 | 5～7 | 93.5 |
| 098-08 | 98.0～99.0 | 9.0～11.0 | 5.0 | 0.5 | 5～7 | 93.5 |
| 092-20 | 91.0～93.0 | 21.0～27.0 | 5.0 | 0.5 | 5～7 | 93.5 |
| 094-27 | 94.0～96.0 | 22.0～28.0 | 5.0 | 0.5 | 5～7 | 93.5 |
| 096-27 | 96.0～98.0 | 23.0～29.0 | 5.0 | 0.5 | 5～7 | 93.5 |
| 100-27 | 99.0～100.0 | 22.0～28.0 | 5.0 | 0.7 | / | 93.5 |
| 092-35 | 91.0～93.0 | 30.0～36.0 | 5.0 | 0.3 | 5～7 | 93.5 |
| 100-35 | 99.0～100.0 | 35.0～43.0 | 5.0 | 0.7 | 5～7 | 93.5 |
| 098-60 | 98.0～99.0 | 58.0～68.0 | 5.0 | 0.5 | 5～7 | 93.5 |
| 100-60 | 99.0～100.0 | 58.0～68.0 | 5.0 | 0.7 | 5～7 | 93.5 |
| 100-70 | 99.0～100.0 | 68.0～78.0 | 5.0 | 0.7 | 5～7 | 93.5 |
Packing:
paper-plastic composite bag, with plastic film inner bag, net weight of each bag is 20kg&25kg.
Application:
Mainly used in textile pulp, paper binder, rewetting binder, surface sizing agent for paper, pigment carrier, Adhesives for architectural coatings, adhesives and additives for building materials, coating agents for seeds and pharmaceuticals, adhesives for inorganic and electronic products, Water-soluble film, cosmetic additive, stabilizer for vinyl acetate emulsion polymerization and vinyl chloride suspension polymerization, temporary protective film etc.
Except CHUANWEI PVA 088-05,088-20,088-50,We can also supply Titanium Dioxide Rutile,Titanium Dioxide Anatase,Iron Oxide Pigments,Carbon Black N330,Sodium Tripolyphosphate 94%, Sodium Hexametaphosphate 68%,PVC Resin, PVC Paste Resin,Bottle Grade PET Resin,Chrome Oxide Green etc.